As the kettle excavated from a site in Hwangnam-dong, Gyeongju was presumed to have been used as a melting crucible in a glass production workplace, we decided to prove its usage be scientific analysis. First, we performed conservation treatment to find the original status of the kettle, and then SEM-EDS and XRD analysis of the five corrosions created on the surface of the kettle. The fragment of the spout, which played a crucial role for the kettle to be considered as a melting crucible, was discovered during the conservation treatment. So the mouth rim of the kettle was restored to perfection. When we observed the microstructure of the metal sample, it was proved to be cast iron gradually cooled without heat treatment. In the corrosion products, the main components were Fe and O and other components such as P, Si, Ca, and S were found. The main compounds were quartz, vivianite, goetheite, akaganite, lepidocrocite, hematite, etc. Although these components were used as raw materials for making glass, these were found not in the melting status but mere raw materials. This can be an evidence to show these site where the kettle was excavated had been a class production workplace. However, it is not sure that the kettle was used as a melting crucible. Moreover, if we consider the organic mold and sand clay accumulated in the well site when the kettle was excavated at first, we can see this as a formative factor of the corrosions of the kettle. Therefore, we concluded that the kettle is a typical cast iron and was not used as a metal crucible of glass. -- MCI